Olefin-Based Polymer

ABSTRACT

The present invention relates to an olefin-based polymer satisfying conditions as follow: (1) a melt index (MI, 190° C., 2.16 kg load conditions) is from 0.1 g/10 min to 10.0 g/10 min, (2) a density (d) is from 0.860 g/cc to 0.880 g/cc, and (3) T(90)−T(50)≤50 and T(95)−T(90)≥10 are satisfied when measured by a differential scanning calorimetry precise measurement method (SSA). The olefin-based polymer according to the present invention is a low-density olefin-based polymer introducing a highly crystalline region and showing high mechanical rigidity.

CROSS-REFERENCE TO RELATED APPLICATIONS

The present application is a national stage entry under 35 U.S.C. § 371 of International Application No. PCT/KR2020/013275 filed on Sep. 28, 2020, which claims priority from Korean Patent Application No. 10-2019-0121152 filed on Sep. 30, 2019, all the disclosures of which are incorporated herein by reference.

TECHNICAL FIELD

The present invention relates to an olefin-based polymer, and more particularly, to a low-density olefin-based polymer introducing a highly crystalline region and showing high mechanical rigidity.

BACKGROUND ART

Polyolefin has excellent moldability, heat resistance, mechanical properties, sanitary quality, permeability of water vapor and appearance characteristics of a molded article, and is widely used as an extrusion molded article, blow molded article and injection molded article. However, there are problems in that polyolefin, particularly, polyethylene has no polar group in a molecule, and has low compatibility with a polar resin such as nylon and poor adhesiveness with a polar resin and a metal. As a result, it has been difficult to blend polyolefin with a polar resin and a metal or laminate with such materials for use. In addition, the molded article of polyolefin has defects of low surface hydrophilicity and antistatic properties.

In order to solve such problems and raise affinity with respect to polar materials, a method of grafting a monomer containing a polar group onto polyolefin through radical polymerization has been widely used. However, according to this method, crosslinking and molecular branch in the molecule of polyolefin may be cleaved during grafting reaction, and the viscosity balance between a graft polymer and a polar resin is not good, and miscibility therebetween is low. In addition, there are problems in that due to gel components produced in a molecule by crosslinking or foreign materials produced by the cleavage of a molecular chain, the appearance characteristics of a molded article is poor.

In addition, as a method for preparing an olefin polymer such as an ethylene homopolymer, an ethylene/α-olefin copolymer, a propylene homopolymer and a propylene/α-olefin copolymer, a method of copolymerizing a polar monomer in the presence of a metal catalyst such as a titanium catalyst and a vanadium catalyst has been used. However, in case of copolymerizing a polar monomer using such a metal catalyst, there are problems of attaining wide molecular weight distribution or composition distribution and low polymerization activity.

In addition, as another method, a polymerization method in the presence of a metallocene catalyst formed using a transition metal compound such as zircononocene dichloride and an organoaluminum oxy compound (aluminoxane) is known. In case of using a metallocene catalyst, an olefin polymer with a high molecular weight is obtained in high activity, and the olefin polymer thus produced has narrow molecular weight distribution and narrow composition distribution.

In addition, as a method of preparing polyolefin containing a polar group, a method of using a metallocene catalyst using a metallocene compound having a ligand of a non-crosslinked cyclopentadienyl group, a crosslinked or non-crosslinked bis indenyl group, or an ethylene crosslinked unsubstituted indenyl group/fluorenyl group as a catalyst, is known. However, this method has defects of very low polymerization activity. Accordingly, a method of protecting a polar group by a protecting group is performed, but in case of introducing a protecting group, this protecting group is required to be removed after reaction, resulting in a complicated process.

An ansa-metallocene compound is an organometal compound including two ligands connected by a bridge group, and due to the bridge group, the rotation of the ligands is prevented, and the activity and structure of a metal center is determined.

Such an ansa-metallocene compound is used as a catalyst for preparing an olefin-based homopolymer or copolymer. Particularly, it is known that an ansa-metallocene compound including a cyclopentadienyl-fluorenyl ligand may produce polyethylene having a high molecular weight, and through this, the microstructure of polypropylene may be controlled.

In addition, it is known that an ansa-metallocene compound including an indenyl ligand has excellent activity and may produce polyolefin having improved stereoregularity.

As described above, various studies on an ansa-metallocene compound capable of controlling the microstructure of an olefin-based polymer have been conducted, but the degrees are not yet enough.

DISCLOSURE OF THE INVENTION Technical Problem

The task to be solved of the present invention is to provide a low-density olefin-based polymer obtained by polymerizing an olefin-based monomer by injecting a hydrogen gas using a transition metal catalyst, thereby introducing a highly crystalline region and showing high mechanical rigidity.

Technical Solution

To solve the above tasks, the present invention provides an olefin-based polymer satisfying the following conditions (1) to (3):

(1) a melt index (MI, 190° C., 2.16 kg load conditions) is from 0.1 g/10 min to 10.0 g/10 min, (2) a density (d) is from 0.860 g/cc to 0.880 g/cc, and (3) T(90)−T(50) 50 and T(95)−T(90)≥10 are satisfied when measured by a differential scanning calorimetry precise measurement method (SSA),

wherein T(50), T(90) and T(95) are temperatures at which 50%, 90%, and 95% of the olefin-based polymer are melted, respectively, when fractionating a temperature-heat capacity curve from measurement results by the differential scanning calorimetry precise measurement method (SSA).

Advantageous Effects

The olefin-based polymer according to the present invention is a low-density olefin-based polymer, wherein a highly crystalline region is introduced, and high mechanical rigidity is shown.

BRIEF DESCRIPTION ON DRAWINGS

FIG. 1 is a graph showing measured results of a melting temperature using differential scanning calorimetry (DSC) on a polymer of Example 1.

FIG. 2 is a graph showing measured results of a melting temperature using differential scanning calorimetry (DSC) on a polymer of Comparative Example 1.

FIG. 3 is a graph showing measured results by a differential scanning calorimetry precise measurement method (SSA) on a polymer of Example 1.

FIG. 4 is a graph showing measured results by a differential scanning calorimetry precise measurement method (SSA) on a polymer of Comparative Example 1.

FIG. 5 is a graph showing T(50), T(90), and T(95) after fractionating measured results by a differential scanning calorimetry precise measurement method (SSA) on a polymer of Example 1.

FIG. 6 is a graph showing T(50), T(90), and T(95) after fractionating measured results by a differential scanning calorimetry precise measurement method (SSA) on a polymer of Comparative Example 1.

BEST MODE FOR CARRYING OUT THE INVENTION

Hereinafter, the present invention will be described in more detail to assist the understanding of the present invention.

It will be understood that words or terms used in the present disclosure and claims shall not be interpreted as the meaning defined in commonly used dictionaries. It will be further understood that the words or terms should be interpreted as having a meaning that is consistent with their meaning in the context of the relevant art and the technical idea of the invention, based on the principle that an inventor may properly define the meaning of the words or terms to best explain the invention.

The term “polymer” used in the present disclosure means a polymer compound prepared by polymerizing monomers which are the same or different types. The common term “polymer” includes a term “interpolymer” as well as “homopolymer”, “copolymer” and “terpolymer”. In addition, the term “interpolymer” means a polymer prepared by polymerizing two or more different types of monomers. The common term “interpolymer” includes a term “copolymer” (commonly used to refer a polymer prepared from two different monomers) and a term “terpolymer” (commonly used to refer a polymer prepared from three different monomers). The term “interpolymer” includes a polymer prepared by polymerizing four or more types of monomers.

The olefin-based polymer according to the present invention satisfies the (1) to (3) below.

(1) a melt index (MI, 190° C., 2.16 kg load conditions) is from 0.1 g/10 min to 10.0 g/10 min, (2) a density (d) is from 0.860 g/cc to 0.880 g/cc, and (3) T(90)−T(50)≤50 and T(95)−T(90)≥10 are satisfied when measured by a differential scanning calorimetry precise measurement method (SSA).

Here, T(50), T(90) and T(95) are temperatures at which 50%, 90%, and 95% of the olefin-based polymer are melted, respectively, when fractionating a temperature-heat capacity curve from measurement results by the differential scanning calorimetry precise measurement method (SSA).

The olefin-based polymer according to the present invention has a very low density and introduces a highly crystalline region when compared with a common conventional olefin-based polymer, and in case of having the same degrees of density and melt index (MI, 190° C., 2.16 kg load conditions), even higher tensile strength and tearing strength may be shown. The olefin-based polymer according to the present invention is prepared by a preparation method including a step of polymerizing an olefin-based monomer by injecting a hydrogen gas in the presence of a catalyst composition for polymerizing olefin, and according to the injection of the hydrogen gas during polymerization, a highly crystalline region is introduced, and excellent mechanical rigidity is shown.

The melt index (MI) may be controlled by controlling an amount of the comonomer used and that of a catalyst used in the process of polymerizing an olefin-based polymer and influences the mechanical properties and impact strength of the olefin-based polymer, and its moldability. In the present disclosure, the melt index is measured under low-density conditions of 0.860 g/cc to 0.880 g/cc according to ASTM D1238 at 190° C. and 2.16 kg load conditions, and may show 0.1 g/10 min to 10 g/10 min, particularly, 0.3 g/10 min to 9 g/10 min, more particularly, 0.4 g/10 min to 7 g/10 min.

Meanwhile, the density may be 0.850 g/cc to 0.890 g/cc, particularly, 0.850 g/cc to 0.880 g/cc, more particularly, 0.860 g/cc to 0.875 g/cc.

Generally, the density of an olefin-based polymer is influenced by the type and amount of a monomer used for polymerization, a polymerization degree, etc., and in case of a copolymer, the influence by the amount of a comonomer is significant. The olefin-based polymer of the present invention is polymerized using a catalyst composition including a transition metal compound having a characteristic structure, and a large amount of comonomer may be introduced. Accordingly, the olefin-based polymer of the present invention may have a low density as in the above-described range.

In addition, the olefin-based polymer may satisfy, when measured by a differential scanning calorimetry precise measurement method (SSA), T(90)−T(50)≤50 and T(95)−T(90)≥10, particularly, 20≤T(90)−T(50)≤45 and 10≤T(95)−T(90)≤30, more particularly, 30≤T(90)−T(50)≤40 and 10≤T(95)−T(90)≤20.

The T(50), T(90) and T(95) are temperatures at which 50%, 90%, and 95% of the olefin-based polymer are melted, respectively, when fractionating a temperature-heat capacity curve from measurement results by the differential scanning calorimetry precise measurement method (SSA).

Generally, the measurement of a melting temperature (Tm) using differential scanning calorimetry is performed by a first cycle including heating to a temperature higher by about 30° C. than the melting temperature (Tm) at a constant rate, and cooling to a temperature lower by about 30° C. than a glass transition temperature (Tg) at a constant rate and a second cycle to obtain the peak of a standard melting temperature (Tm). The differential scanning calorimetry precise measurement method (SSA) is a method of obtaining more accurate crystal information by undergoing a process of heating immediately before the peak of a melting temperature (Tm) and cooling after the first cycle using differential scanning calorimetry (DSC), and repeatedly performing heating to a temperature reduced by about 5° C. and cooling (Eur. Polym. J. 2015, 65, 132).

In case of introducing a small amount of a highly crystalline region to an olefin-based polymer, a high temperature melting peak may not be shown when measured by a melting temperature using general differential scanning calorimetry (DSC) but may be measured through the differential scanning calorimetry precise measurement method (SSA).

In addition, the olefin-based polymer according to an embodiment of the present invention may additionally satisfy the conditions of (4) a weight average molecular weight (Mw) of 10,000 g/mol to 500,000 g/mol, and particularly, the weight average molecular weight (Mw) may be 30,000 g/mol to 300,000 g/mol, more particularly, 50,000 g/mol to 200,000 g/mol. In the present invention, the weight average molecular weight (Mw) is a polystyrene conversion molecular weight analyzed by gel permeation chromatography (GPC).

In addition, the olefin-based polymer according to an embodiment of the present invention may additionally satisfy the conditions of (5) molecular weight distribution (MWD) which is the ratio (Mw/Mn) of a weight average molecular weight (Mw) and a number average molecular weight (Mn), of 0.1 to 6.0, and the molecular weight distribution (MWD) may particularly be 1.0 to 4.0, more particularly, 2.0 to 3.0.

In addition, the olefin-based polymer according to an embodiment of the present invention may satisfy the conditions of (6) a melting temperature (Tm) of 20° C. to 70° C. when measured by differential scanning calorimetry (DSC), wherein the melting temperature (Tm) may particularly be 25° C. to 60° C., more particularly, 25° C. to 50° C.

The olefin-based polymer may be any homopolymer selected from an olefin-based monomer, particularly, an alpha-olefin-based monomer, a cyclic olefin-based monomer, a diene olefin-based monomer, a triene olefin-based monomer and a styrene-based monomer, or a copolymer of two or more. More particularly, the olefin-based polymer may be a copolymer of ethylene with alpha-olefin of 3 to 12 carbon atoms, or a copolymer with alpha-olefin of 3 to 10 carbon atoms.

The alpha-olefin comonomer may include any one selected from the group consisting of propylene, 1-butene, 1-pentene, 4-methyl-1-pentene, 1-hexene, 1-heptene, 1-octene, 1-decene, 1-undecene, 1-dodecene, 1-tetradecene, 1-hexadecene, 1-eicosene, norbornene, norbonadiene, ethylidene norbornene, phenyl norbornene, vinyl norbornene, dicyclopentadiene, 1,4-butadiene, 1,5-pentadiene, 1,6-hexadiene, styrene, alpha-methylstyrene, divinylbenzene and 3-chloromethylstyrene, or mixtures of two or more thereof.

More particularly, the olefin-based copolymer according to an embodiment of the present invention may be a copolymer of ethylene with propylene, ethylene with 1-butene, ethylene with 1-hexene, ethylene with 4-methyl-1-pentene or ethylene with 1-octene, and more particularly, the olefin copolymer according to an embodiment of the present invention may be a copolymer of ethylene with 1-butene.

If the olefin-based polymer is the copolymer of ethylene and alpha-olefin, the amount of the alpha-olefin may be 90 wt % or less, more particularly, 70 wt % or less, further more particularly, 5 wt % to 60 wt %, further more particularly, 20 wt % to 50 wt % based on the total weight of the copolymer. If the alpha-olefin is included in the range, the achievement of the above-described physical properties may be easy.

The olefin-based polymer according to an embodiment of the present invention having the above-described physical properties and configurational characteristics may be prepared through continuous solution polymerization reaction for polymerizing an olefin-based monomer by injecting a hydrogen gas in the presence of a metallocene catalyst composition including one or more types of transition metal compounds in a single reactor. Accordingly, in the olefin-based polymer according to an embodiment of the present invention, a block composed by linearly connecting two or more repeating units derived from any one monomer among monomers constituting a polymer is not formed in the polymer. That is, the olefin-based polymer according to the present invention may not include a block copolymer, but may be selected from the group consisting of a random copolymer, an alternating copolymer and a graft copolymer, more particularly, a random copolymer.

In an embodiment of the present invention, the injection amount of the hydrogen gas may be 0.35 to 3 parts by weight, particularly, 0.4 to 2 parts by weight, more particularly, 0.45 to 1.5 parts by weight based on 1 part by weight of an olefin-based monomer injected into a reaction system. In addition, in an embodiment of the present invention, if the olefin-based polymer is polymerized by continuous solution polymerization, the hydrogen gas may be injected in an amount of 0.35 to 3 kg/h, particularly, 0.4 to 2 kg/h, more particularly, 0.45 to 1.5 kg/h based on 1 kg/h of the olefin-based monomer injected into a reaction system.

In addition, in another embodiment of the present invention, in case where the olefin-based polymer is a copolymer of ethylene and alpha-olefin, the hydrogen gas may be injected in an amount of 0.8 to 3 parts by weight, particularly, 0.9 to 2.8 parts by weight, more particularly, 1 to 2.7 parts by weight based on 1 part by weight of ethylene. In addition, in an embodiment of the present invention, in case where the olefin-based polymer is a copolymer of ethylene and alpha-olefin and is polymerized by continuous solution polymerization, the hydrogen gas may be injected into a reaction system in an amount of 0.8 to 3 kg/h, particularly, 0.9 to 2.8 kg/h, more particularly, 1 to 2.7 kg/h based on 1 kg/h of ethylene.

If polymerization is performed under conditions of injecting the above-described amount range of the hydrogen gas, the olefin-based polymer of the present invention may satisfy the above-described physical properties.

Particularly, the olefin-based copolymer of the present invention may be obtained by a preparation method including a step of polymerizing an olefin-based monomer by injecting a hydrogen gas in the presence of a catalyst composition for polymerizing olefin, including a transition metal compound of Formula 1 below.

However, in the preparation of the olefin-based polymer according to an embodiment of the present invention, it should be understood that the range of the structure of the transition metal compound of Formula 1 is not limited to a specific disclosed type, but all changes, equivalents or substituents included in the spirit and technical range of the present invention are included.

In Formula 1,

R₁ groups are the same or different and each independently hydrogen, alkyl of 1 to 20 carbon atoms, alkenyl of 2 to 20 carbon atoms, aryl, silyl, alkylaryl, arylalkyl, or metalloid radical of a metal in group 4, which is substituted with hydrocarbyl, and two R₁ groups may be connected with each other by alkylidene radical containing alkyl of 1 to 20 carbon atoms or aryl radical of 6 to 20 carbon atoms to form a ring;

R₂ groups are the same or different and each independently hydrogen; halogen; alkyl of 1 to 20 carbon atoms; aryl; alkoxy; aryl oxy; or amido radical, and two R₂ groups may be connected with each other to form an aliphatic ring or an aromatic ring;

R₃ groups are the same or different and each independently hydrogen; halogen; alkyl of 1 to 20 carbon atoms; or a nitrogen-containing aliphatic or aromatic ring, which is unsubstituted or substituted with aryl radical, in case where multiple substituents are present, two or more substituents among the substituents may be connected with each other to form an aliphatic or aromatic ring;

M is a transition metal in group 4; and

Q₁ and Q₂ are each independently halogen; alkyl of 1 to 20 carbon atoms; alkenyl; aryl; alkylaryl; arylalkyl; alkyl amido of 1 to 20 carbon atoms; aryl amido; or alkylidene radical of 1 to 20 carbon atoms.

In addition, in another embodiment of the present invention, in Formula 2, R₁ and R₂ may be the same or different and each independently hydrogen; alkyl of 1 to 20 carbon atoms; aryl; or silyl,

R₃ groups may be the same or different and may be alkyl of 1 to 20 carbon atoms; alkenyl of 2 to 20 carbon atoms; aryl; alkylaryl; arylalkyl; alkoxy of 1 to 20 carbon atoms; aryloxy; or amido, and two or more R₃ groups may be connected with each other to form an aliphatic or aromatic ring;

Q₁ and Q₂ may be the same or different and each independently halogen; alkyl of 1 to 20 carbon atoms; alkyl amido of 1 to 20 carbon atoms; or aryl amido, and

M may be a transition metal in group 4.

The transition metal compound represented by Formula 1 has characteristics in which a metal site is connected by a cyclopentadienyl (Cp) ligand introducing tetrahydroquinoline, and a narrow Cp-M-N angle and a wide Q₁-M-Q₂ (Q₃-M-Q₄) angle to which a monomer goes near, are maintained. In addition, according to the bonding of a ring type, Cp, tetrahydroquinoline, nitrogen and a metal site are connected in order, and more stable and rigid five-member ring structure is formed. Accordingly, in case of activating such compounds by reacting with a co-catalyst such as methylaluminoxane and B(C₆F₅)₃ and then, applying thereof to olefin polymerization, the polymerization of an olefin-based polymer having the characteristics of high activity, high molecular weight and high copolymerization properties may be achieved even at a high polymerization temperature.

Each substituent defined in the present disclosure will be explained in detail as follows.

The term “hydrocarbyl group” used in the present disclosure means a monovalent hydrocarbon group of 1 to 20 carbon atoms, which is composed of only carbon and hydrogen irrespective of its structure, such as alkyl, aryl, alkenyl, alkynyl, cycloalkyl, alkylaryl and arylalkyl, unless otherwise referred to.

The term “halogen” used in the present disclosure means fluorine, chlorine, bromine or iodine, unless otherwise referred to.

The term “alkyl” used in the present disclosure means a hydrocarbon residual group of a linear chain or branched chain, unless otherwise referred to.

The term “cycloalkyl” used in the present disclosure represents cyclic alkyl including cyclopropyl, etc., unless otherwise referred to.

The term “alkenyl” used in the present disclosure means an alkenyl group of a linear chain or branched chain, unless otherwise referred to.

The branched chain may be alkyl of 1 to 20 carbon atoms; alkenyl of 2 to 20 carbon atoms; aryl of 6 to 20 carbon atoms; alkylaryl of 7 to 20 carbon atoms; or arylalkyl of 7 to 20 carbon atoms.

The term “aryl” used in the present invention represents, unless otherwise referred to, an aromatic group of 6 to 20 carbon atoms, particularly, phenyl, naphthyl, anthryl, phenanthryl, chrysenyl, pyrenyl, anthracenyl, pyridyl, dimethylanilinyl, anisolyl, etc., without limitation.

The alkylaryl group means an aryl group substituted with the alkyl group.

The arylalkyl group means an alkyl group substituted with the aryl group.

The cyclic group (or heterocyclic group) means a monovalent aliphatic or aromatic hydrocarbon group having 5 to 20 ring-forming carbon atoms and including one or more heteroatoms, and may be a single ring or a condensed ring of two or more rings. In addition, the heterocyclic group may be unsubstituted or substituted with an alkyl group. Examples thereof may include indoline, tetrahydroquinoline, etc., but the present invention is not limited thereto.

The alkyl amino group means an amino group substituted with the alkyl group, and includes a dimethylamino group, a diethylamino group, etc., without limitation.

According to an embodiment of the present invention, the aryl group may preferably have 6 to 20 carbon atoms, and may particularly be phenyl, naphthyl, anthracenyl, pyridyl, dimethylanilinyl, anisolyl, etc., without limitation.

In the present disclosure, the silyl may be silyl unsubstituted or substituted with alkyl of 1 to 20 carbo atoms, for example, silyl, trimethylsilyl, triethylsilyl, tripropylsilyl, tributylsilyl, trihexylsilyl, triisopropylsilyl, triisobutylsilyl, triethoxysilyl, triphenylsilyl, tris(trimethylsilyl)silyl, etc., without limitation.

The compound of Formula 1 may be Formula 1-1 below, without limitation.

Besides, the compound may have various structures within the range defined in Formula 1.

The transition metal compound of Formula 1 may introduce a large amount of alpha-olefin as well as low-density polyethylene due to the structural characteristics of a catalyst, and a low-density polyolefin copolymer with a degree of 0.850 g/cc to 0.890 g/cc may be prepared.

The transition metal compound of Formula 1 may be prepared by, for example, a method below.

In Reaction 1, R₁ to R₃, M, Q₁ and Q₂ are the same as defined in Formula 1.

Formula 1 may be prepared by a method disclosed in Patent Laid-open No. 2007-0003071, and all contents of the patent document are included in the present disclosure.

The transition metal compound of Formula 1 may be used as a catalyst of polymerization reaction as a composition type additionally including one or more among the co-catalyst compounds represented by Formula 2, Formula 3, and Formula 4 below.

[Al(R₄)—O]_(a)—  [Formula 2]

A(R₄)₃  [Formula 3]

[L-H]+[W(D)₄]⁻ or [L]⁺[W(D)₄]⁻  [Formula 4]

In Formulae 2 to 3,

R₄ groups may be the same or different from each other and each independently selected from the group consisting of halogen, hydrocarbyl of 1 to 20 carbon atoms, and halogen-substituted hydrocarbyl of 1 to 20 carbon atoms,

A is aluminum or boron,

D groups are each independently aryl of 6 to 20 carbon atoms or alkyl of 1 to 20 carbon atoms, of which one or more hydrogen atoms may be substituted with substituents, wherein the substituent is at least any one selected from the group consisting of halogen, hydrocarbyl of 1 to 20 carbon atoms, alkoxy of 1 to 20 carbon atoms and aryloxy of 6 to 20 carbon atoms,

H is a hydrogen atom,

L is a neutral or cationic Lewis acid,

W is an element in group 13, and

a is an integer of 2 or more.

Examples of the compound represented by Formula 2 may include alkylaluminoxane such as methylaluminoxane (MAO), ethylaluminoxane, isobutylaluminoxane and butylalminoxane, and a modified alkylaluminoxane obtained by mixing two or more types of the alkylaluminoxane, particularly, methylaluminoxane, modified methylaluminoxane (MMAO).

Examples of the compound represented by Formula 3 may include trimethylaluminum, triethylaluminum, triisobutylaluminum, tripropylaluminum, tributylaluminum, dimethylchloroaluminum, triisopropylaluminum, tri-s-butylaluminum, tricyclopentylaluminum, tripentylaluminum, triisopentylaluminum, trihexylaluminum, trioctylaluminum, ethyldimethylaluminum, methyldiethylaluminum, triphenylaluminum, tri-p-tolylaluminum, dimethylaluminummethoxide, dimethylaluminumethoxide, trimethylboron, triethylboron, triisobutylboron, tripropylboron, tributylboron, etc. and particularly, may be selected from trimethylaluminum, triethylaluminum and triisobutylaluminum.

Examples of the compound represented by Formula 4 may include triethylammoniumtetraphenylboron, tributylammoniumtetraphenylboron, trimethylammoniumtetraphenylboron, tripropylammoniumtetraphenylboron, trimethylammoniumtetra(p-tolyl)boron, trimethylammoniumtetra(o,p-dimethylphenyl)boron, tributylammoniumtetra(p-trifluoromethylphenyl)boron, trimethylammoniumtetra(p-trifluoromethylphenyl)boron, tributylammoniumtetrapentafluorophenylboron, N,N-diethylaniliumtetraphenylboron, N,N-diethylaniliumtetrapentafluorophenylboron, diethylammoniumtetrapentafluorophenylboron, triphenylphosphoniumtetraphenylboron, trimethylphosphoniumtetraphenylboron, dimethylanilium tetrakis(pentafluorophenyl) borate, triethylammoniumtetraphenylaluminum, tributylammoniumtetraphenylaluminum, trimethylammoniumtetraphenylaluminum, tripropylammoniumtetraphenylaluminum, trimethylammoniumtetra(p-tolyl)aluminum, tripropylammoniumtetra(p-tolyl)aluminum, triethylammoniumtetra(o,p-dimethylphenyl)aluminum, tributylammoniumtetra(p-trifluoromethylphenyl)aluminum, trimethylammoniumtetra(p-trifluoromethylphenyl)aluminum, tributylammoniumtetrapentafluorophenylaluminum, N,N-diethylaniliniumtetraphenylaluminum, N,N-diethylaniliumtetrapentafluorophenylaluminum, diethylammoniumtetrapentatetraphenylaluminum, triphenylphosphoniumtetraphenylaluminum, trimethylphosphoniumtetraphenylaluminum, tripropylammoniumtetra(p-tolyl)boron, triethylammoniumtetra(o,p-dimethylphenyl) boron, triphenylcarboniumtetra(p-trifluoromethylphenyl)boron, or triphenylcarboniumtetrapentafluorophenylboron.

The catalyst composition may be prepared by, as a first method, a preparation method including a step of obtaining a mixture by contacting the transition metal compound represented by Formula 1 with the compound represented by Formula 2 or Formula 3; and a step of adding the compound represented by Formula 4 to the mixture.

In addition, the catalyst composition may be prepared by, as a second method, a method of making contacting of the transition metal compound represented by Formula 1 with the compound represented by Formula 4.

In the first method in the preparation method of the catalyst composition, the molar ratio of the transition metal compound represented by Formula 1 and the transition metal compound represented by Formula 2/the compound represented by Formula 2 or Formula 3 may be 1/5,000 to 1/2, particularly, 1/1,000 to 1/10, more particularly, 1/500 to 1/20. If the molar ratio of the transition metal compound represented by Formula 1/the compound represented by Formula 2 or Formula 3 is greater than 1/2, the amount of an alkylating agent is too small, and the alkylation of a metal compound may be incompletely carried out, and if the molar ratio is less than 1/5,000, the alkylation of the metal compound may be achieved, but the activation of the alkylated metal compound may be incompletely carried out due to the side reactions between an excessive amount of the alkylating agent remained and an activating agent which is the compound of Formula 4. In addition, the molar ratio of the transition metal compound represented by Formula 1/the compound represented by Formula 4 may be 1/25 to 1, particularly, 1/10 to 1, more particularly, 1/5 to 1. If the molar ratio of the transition metal compound represented by Formula 1/the compound represented by Formula 4 is greater than 1, the amount of an activating agent is relatively small, and the activation of the metal compound may be incompletely carried out, and thus, the activity of the catalyst composition may be deteriorated. If the molar ratio is less than 1/25, the activation of the metal compound may be completely carried out, but due to the excessive amount of the activating agent remained, it would not be economical considering the unit cost of the catalyst composition, or the purity of a polymer produced may be degraded.

In the second method in the preparation method of the catalyst composition, the molar ratio of the transition metal compound represented by Formula 1/the compound represented by Formula 4 may be 1/10,000 to 1/10, particularly, 1/5,000 to 1/100, more particularly, 1/3,000 to 1/500. If the molar ratio is greater than 1/10, the amount of an activating agent is relatively small, and the activation of the metal compound may be incompletely carried out, and the activity of the catalyst composition thus produced may be degraded. If the molar ratio is less than 1/10,000, the activation of the metal compound may be completely carried out, but due to the excessive amount of the activating agent remained, it would not be economical considering the unit cost of the catalyst composition, or the purity of a polymer produced may be degraded.

As the reaction solvent during preparing the catalyst composition, a hydrocarbon-based solvent such as pentane, hexane, and heptane, or an aromatic solvent such as benzene and toluene may be used.

In addition, the catalyst composition may include the transition metal compound and the co-catalyst compound in a supported type on a support.

Any supports used in a metallocene-based catalyst may be used as the support without specific limitation. Particularly, the support may be silica, silica-alumina or silica-magnesia, and any one among them or mixtures of two or more thereof may be used.

In case where the support is silica among them, since a silica support and the functional group of the metallocene compound of Formula 1 may form a chemical bond, there is no catalyst separated from the surface during an olefin polymerization process. As a result, the generation of fouling, by which polymer particles are agglomerated on the wall side of a reactor or from each other during the preparation process of an olefin-based copolymer, may be prevented. In addition, the particle shape and apparent density of a polymer of the olefin-based copolymer prepared in the presence of a catalyst including the silica support are excellent.

More particularly, the support may be silica or silica-alumina, including a highly reactive siloxane group and dried at a high temperature through a method of drying at a high temperature, etc.

The support may further include an oxide, a carbonate, a sulfate, or a nitrate component such as Na₂O, K₂CO₃, BaSO₄ and Mg(NO₃)₂.

The polymerization reaction for polymerizing the olefin-based monomer may be achieved by a common process applied to the polymerization of an olefin monomer such as continuous solution polymerization, bulk polymerization, suspension polymerization, slurry polymerization and emulsion polymerization.

The polymerization reaction of the olefin monomer may be performed in an inert solvent, and as the inert solvent, benzene, toluene, xylene, cumene, heptane, cyclohexane, methylcyclohexane, methylcyclopentane, n-hexane, 1-hexene, and 1-octene may be used, without limitation.

The polymerization of the olefin-based polymer may be performed at a temperature of about 25° C. to about 500° C., particularly, at a temperature of 80° C. to 250° C., more preferably, 100° C. to 200° C. In addition, the reaction pressure during the polymerization may be 1 kgf/cm² to 150 kgf/cm², preferably, 1 kgf/cm² to 120 kgf/cm², more preferably, 5 kgf/cm² to 100 kgf/cm².

The olefin-based polymer of the present invention has improved physical properties, and accordingly, may be useful for hollow molding, extrusion molding or injecting molding in various fields and uses for packing, construction, household items, etc. including materials for cars, wires, toys, fibers, and medical, and particularly, useful for cars requiring excellent impact strength.

In addition, the olefin-based polymer of the present invention may be usefully used for the manufacture of a molded article.

The molded article may be a blow molding molded article, an inflation molded article, a cast molded article, an extrusion laminate molded article, an extrusion molded article, a foam molded article, an injection molded article, a sheet, a film, a fiber, a monofilament, a nonwoven fabric, etc.

MODE FOR CARRYING OUT THE INVENTION Examples

Hereinafter, embodiments of the present invention will be explained in detail so that a person skilled in the art where the present invention belongs could easily perform. However, the present invention may be accomplished in various different types and is not limited to the embodiments explained herein.

Preparation Example 1: Preparation of Transition Metal Compound a

(1) Preparation of 8-(2,3,4,5-tetramethyl-1,3-cyclopentadienyl)-1,2,3,4-tetrahydroquinoline

(i) Preparation of Lithium Carbamate

1,2,3,4-tetrahydroquinoline (13.08 g, 98.24 mmol) and diethyl ether (150 mL) were put in a shlenk flask. Into a low-temperature bath of −78° C. obtained by dry ice and acetone, the shlenk flask was immersed and stirred for 30 minutes. Then, n-BuLi (39.9 mL, 2.5 M, 98.24 mmol) was injected under a nitrogen atmosphere via a syringe, and a light yellow slurry was formed. Then, the flask was stirred for 2 hours, and the temperature of the flask was elevated to room temperature while removing a butane gas produced. The flask was immersed again into the low-temperature bath of −78° C. to reduce the temperature, and a CO₂ gas was injected. According to the injection of the carbon dioxide gas, the slurry disappeared into a transparent solution. The flask was connected with a bubbler, and the temperature was elevated to room temperature while removing the carbon dioxide gas. After that, remaining CO₂ gas and solvents were removed under vacuum. After transporting the flask to a dry box, pentane was added thereto, followed by vigorous stirring and filtering to obtain lithium carbamate as a white solid compound. In the white solid compound, diethyl ether made a coordination bond. In this case, the yield was 100%.

¹H NMR (C₆D₆, C₅D₅N) δ 1.90 (t, J=7.2 Hz, 6H, ether), 1.50 (br s, 2H, quin-CH₂), 2.34 (br s, 2H, quin-CH₂), 3.25 (q, J=7.2 Hz, 4H, ether), 3.87 (br, s, 2H, quin-CH₂), 6.76 (br d, J=5.6 Hz, 1H, quin-CH) ppm

¹³C NMR (C₆D₆): δ 24.24, 28.54, 45.37, 65.95, 121.17, 125.34, 125.57, 142.04, 163.09 (C═O) ppm

(ii) Preparation of 8-(2,3,4,5-tetramethyl-1,3-cyclopentadienyl)-1,2,3,4-tetrahydroquinoline

The lithium carbamate compound (8.47 g, 42.60 mmol) prepared in step (i) above was put in a shlenk flask. Then, tetrahydrofuran (4.6 g, 63.9 mmol) and 45 mL of diethyl ether were added thereto in order. Into a low-temperature bath of −20° C. obtained by acetone and a small amount of dry ice, the shlenk flask was immersed and stirred for 30 minutes, and n-BuLi (25.1 mL, 1.7 M, 42.60 mmol) was injected. In this case, the color of the reaction mixture was changed into red. While continuously maintaining −20° C., stirring was performed for 6 hours. A CeCl₃.2LiCl solution (129 mL, 0.33 M, 42.60 mmol) dissolved in tetrahydrofuran and tetramethylcyclopentanone (5.89 g, 42.60 mmol) were mixed in a syringe and then injected into the flask under a nitrogen atmosphere. In the middle of slowly elevating the temperature of the flask to room temperature, a thermostat was removed after 1 hour, and the temperature was maintained to room temperature. Then, water (15 mL) was added to the flask, and ethyl acetate was put, followed filtering to obtain a filtrate. The filtrate was transported to a separating funnel, and hydrochloric acid (2 N, 80 mL) was added thereto, followed by shaking for 12 minutes. Then, a saturated sodium bicarbonate solution (160 mL) was added to neutralize, and an organic layer was extracted. To the organic layer, anhydrous magnesium sulfate was put to remove moisture, and filtering was conducted. The filtrate was taken, and solvents were removed. The filtrate thus obtained was separated by a column chromatography method using a solvent of hexane and ethyl acetate (v/v, 10:1) to obtain a yellow oil. The yield was 40%.

¹H NMR (C₆D₆): δ 1.00 (br d, 3H, Cp-CH₃), 1.63-1.73 (m, 2H, quin-CH₂), 1.80 (s, 3H, Cp-CH₃), 1.81 (s, 3H, Cp-CH₃), 1.85 (s, 3H, Cp-CH₃), 2.64 (t, J=6.0 Hz, 2H, quin-CH₂), 2.84-2.90 (br, 2H, quin-CH₂), 3.06 (br s, 1H, Cp-H), 3.76 (br s, 1H, N—H), 6.77 (t, J=7.2 Hz, 1H, quin-CH), 6.92 (d, J=2.4 Hz, 1H, quin-CH), 6.94 (d, J=2.4 Hz, 1H, quin-CH) ppm

(2) Preparation of [(1,2,3,4-tetrahydroquinolin-8-yl)tetramethylcyclopentadienyl-η⁵,K—N]titanium dimethyl

(i) Preparation of [(1,2,3,4-tetrahydroquinoline-8-yl)tetramethylcyclopentadienyl-η⁵,K—N]dilithium compound

In a dry box, 8-(2,3,4,5-tetramethyl-1,3-cyclopentadienyl)-1,2,3,4-tetrahydroquinoline (8.07 g, 32.0 mmol) prepared through step (1) above, and 140 mL of diethyl ether were put in a round flask, the temperature was reduced to −30° C., and n-BuLi (17.7 g, 2.5 M, 64.0 mmol) was slowly added while stirring. The reaction was performed for 6 hours while elevating the temperature to room temperature. After that, washing with diethyl ether was conducted several times, and filtering was conducted to obtain a solid. Remaining solvents were removed by applying vacuum to obtain a dilithium compound (9.83 g) as a yellow solid. The yield was 95%.

¹H NMR (C₆D₆, C₅D₅N) δ 2.38 (br s, 2H, quin-CH₂), 2.53 (br s, 12H, Cp-CH₃), 3.48 (br s, 2H, quin-CH₂), 4.19 (br s, 2H, quin-CH₂), 6.77 (t, J=6.8 Hz, 2H, quin-CH), 7.28 (br s, 1H, quin-CH), 7.75 (brs, 1H, quin-CH) ppm

(ii) Preparation of (1,2,3,4-tetrahydroquinolin-8-yl)tetramethylcyclopentadienyl-η⁵,K—N]titanium dimethyl

In a dry box, TiCl₄.DME (4.41 g, 15.76 mmol) and diethyl ether (150 mL) were put in a round flask, and while stirring at −30° C., MeLi (21.7 mL, 31.52 mmol, 1.4 M) was slowly added. After stirring for 15 minutes, the (1,2,3,4-tetrahydroquinolin-8-yl)tetramethylcyclopentadienyl-ηη⁵,K—N]dilithium compound (5.30 g, 15.78 mmol) prepared in step (i) above was put in the flask. While elevating the temperature to room temperature, stirring was conducted for 3 hours. After finishing the reaction, vacuum was applied to remove solvents, and the resultant residue was dissolved in pentane and filtered, and the filtrate was taken. By removing pentane by applying vacuum, a dark brown compound (3.70 g) was obtained. The yield was 71.3%.

¹H NMR (C₆D₆) δ 0.59 (s, 6H, Ti—CH₃), 1.66 (s, 6H, Cp-CH₃), 1.69 (br t, J=6.4 Hz, 2H, quin-CH₂), 2.05 (s, 6H, Cp-CH₃), 2.47 (t, J=6.0 Hz, 2H, quin-CH₂), 4.53 (m, 2H, quin-CH₂), 6.84 (t, J=7.2 Hz, 1H, quin-CH), 6.93 (d, J=7.6 Hz, quin-CH), 7.01 (d, J=6.8 Hz, quin-CH) ppm

¹³C NMR (C₆D₆): δ 12.12, 23.08, 27.30, 48.84, 51.01, 119.70, 119.96, 120.95, 126.99, 128.73, 131.67, 136.21 ppm

Preparation Example 2: Preparation of Transition Metal Compound B

(1) Preparation of 2-methyl-7-(2,3,4,5-tetramethyl-1,3-cyclopentadienyl)indoline

2-methyl-7-(2,3,4,5-tetramethyl-1,3-cyclopentadienyl)indoline was prepared through the same method as in (1) in Preparation Example 1 except for using 2-methylindoline instead of 1,2,3,4-tetrahydroquinoline in (1) of Preparation Example 1. The yield was 19%.

¹H NMR (C₆D₆): δ 6.97 (d, J=7.2 Hz, 1H, CH), δ 6.78 (d, J=8 Hz, 1H, CH), δ 6.67 (t, J=7.4 Hz, 1H, CH), δ 3.94 (m, 1H, quinoline-CH), δ 3.51 (br s, 1H, NH), δ 3.24-3.08 (m, 2H, quinoline-CH₂, Cp-CH), δ 2.65 (m, 1H, quinoline-CH²), δ 1.89 (s, 3H, Cp-CH₃), δ 1.84 (s, 3H, Cp-CH₃), δ 1.82 (s, 3H, Cp-CH₃), S 1.13 (d, J=6 Hz, 3H, quinoline-CH₃), S 0.93 (3H, Cp-CH₃) ppm.

(2) Preparation of [(2-Methylindolin-7-yl)tetramethylcyclopentadienyl-eta5,kapa-N]titanium dimethyl

(i) A dilithium salt compound (compound 4 g) coordinated with 0.58 equivalent of diethyl ether was obtained (1.37 g, 50%) through the same method as in (2) (i) in Preparation Example 1 except for using 2-methyl-7-(2,3,4,5-tetramethyl-1,3-cyclopentadienyl)-indoline (2.25 g, 8.88 mmol) instead of 8-(2, 3, 4, 5-tetramethyl-1,3-cyclopentadienyl)-1,2,3,4-tetrahydroquinoline.

¹H NMR (Pyridine-d8): δ 7.22 (br s, 1H, CH), δ 7.18 (d, J=6 Hz, 1H, CH), δ 6.32 (t, 1H, CH), S 4.61 (brs, 1H, CH), S 3.54 (m, 1H, CH), δ 3.00 (m, 1H, CH), δ 2.35-2.12 (m, 13H, CH, Cp-CH₃), δ 1.39 (d, indoline-CH₃) ppm.

(ii) A titanium compound was prepared through the same method as in (2) (ii) in Preparation Example 1 using the dilithium salt compound (compound 4 g) (1.37 g, 4.44 mmol) prepared in (i) above.

¹H NMR (C₆D₆): δ 7.01-6.96 (m, 2H, CH), δ 6.82 (t, J=7.4 Hz, 1H, CH),

δ 4.96 (m, 1H, CH), δ 2.88 (m, 1H, CH), δ 2.40 (m, 1H, CH), δ 2.02 (s, 3H, Cp-CH₃), δ 2.01 (s, 3H, Cp-CH₃), δ 1.70 (s, 3H, Cp-CH₃), δ 1.69 (s, 3H, Cp-CH₃), δ 1.65 (d, J=6.4 Hz, 3H, indoline-CH₃), S 0.71 (d, J=10 Hz, 6H, TiMe₂-CH₃) ppm.

Example 1

To a 1.5 L continuous process reactor, a hexane solvent (5 kg/h) and 1-butene (0.95 kg/h) were charged, and the temperature of the top of the reactor was pre-heated to 140.7° C. A triisobutylaluminum compound (0.06 mmol/min), the transition metal compound B (0.40 μmol/min) obtained in Preparation Example 2, and a dimethylanilinium tetrakis(pentafluorophenyl) borate co-catalyst (1.20 μmol/min) were injected at the same time into the reactor. Then, a hydrogen gas (15 cc/min) and ethylene (0.87 kg/h) were injected into the reactor, and copolymerization reaction was performed by maintaining 141° C. for 30 minutes or more in a continuous process with a pressure of 89 bar to obtain a copolymer. After drying in a vacuum oven for 12 hours or more, physical properties were measured.

Examples 2 to 5

Copolymers were obtained by performing the same copolymerization reaction as in Example 1 except for changing the amount used of a transition metal compound, the amounts used of a catalyst and a co-catalyst, the reaction temperature, the injection amount of hydrogen and the amount of a comonomer as in Table 1 below.

Comparative Example 1

DF610 of Mitsui Chemicals Inc. was purchased and used.

Comparative Examples 2 to 4

Copolymers were obtained by performing the same copolymerization reaction as in Example 1 except for changing the type of a transition metal compound, the amount used of a transition metal compound, the amounts used of a catalyst and a co-catalyst, the reaction temperature, the injection amount of hydrogen and the amount of a comonomer as in Table 1 below.

Comparative Example 5

DF710 of Mitsui Chemicals Inc. was purchased and used.

Comparative Example 6

DF640 of Mitsui Chemicals Inc. was purchased and used.

Comparative Example 7

EG7447 of Dow Co. was purchased and used.

TABLE 1 Catalyst amount Co-cat. TiBA1 1- Reaction Catalyst used (μmol/ (mmol/ Ethylene Hexane butene Hydrogen temp. type (μmol/min) min) min) (kg/h) (Kg/h) (kg/h) (cc/min) (° C.) Example 1 Transition 0.40 1.20 0.06 0.87 5 0.95 15 141 metal compound B Example 2 Transition 0.60 1.80 0.05 0.87 7 0.93 32 145 metal compound B Example 3 Transition 0.45 1.35 0.04 0.87 7 0.75 15 145 metal compound B Example 4 Transition 0.74 2.22 0.05 0.87 7 0.93 25 150 metal compound B Example 5 Transition 0.55 1.65 0.04 0.87 7 0.84 38 148 metal compound B Comparative Transition 0.78 2.34 0.06 0.87 5 1.15 — 161 Example 2 metal compound B Comparative Transition 0.32 0.96 0.05 0.87 5 0.62 — 145 Example 3 metal compound A Comparative Transition 0.50 1.50 0.06 0.87 5 1.15 10 161 Example 4 metal compound B

Experimental Example 1

With respect to the copolymers of Examples 1 to 5, and Comparative Examples 1 to 4, physical properties were evaluated according to the methods below and are shown in Tables 2 and 3 below.

1) Density of Polymer

Measurement was conducted according to ASTM D-792.

2) Melt Index (MI) of Polymer

Measurement was conducted according to ASTM D-1238 (condition E, 190° C., 2.16 kg load).

3) Weight Average Molecular Weight (Mw, g/Mol) and Molecular Weight Distribution (MWD)

A number average molecular weight (Mn) and a weight average molecular weight (Mw) were measured respectively, using gel permeation chromatography (GPC), and molecular weight distribution was calculated through dividing the weight average molecular weight by the number average molecular weight.

-   -   Column: PL Olexis     -   Solvent: trichlorobenzene (TCB)     -   Flow rate: 1.0 ml/min     -   Specimen concentration: 1.0 mg/ml     -   Injection amount: 200 μl     -   Column temperature: 160° C.     -   Detector: Agilent High Temperature RI detector     -   Standard: Polystyrene (calibrated by cubic function)

4) Melting Temperature (Tm) of Polymer

The melting temperature was obtained using a differential scanning calorimeter (DSC: differential scanning calorimeter 250) manufactured by TA instrument Co. That is, the temperature was elevated to 150° C., kept for 1 minute, and reduced to −100° C., and then, the temperature was elevated again. The apex of a DSC curve was set to the melting point. In this case, the elevating rate and reducing rate of the temperature were controlled to 10° C./min, and the melting temperature was obtained during the second elevation of the temperature.

The DSC graph of the polymer of Example 1 is shown in FIG. 1, and the DSC graph of the polymer of Comparative Example 1 is shown in FIG. 2.

5) High Temperature Melting Peak of Polymer and T(95), T(90) and T(50)

Measurement was conducted by using a differential scanning calorimeter (DSC: differential scanning calorimeter 250) manufactured by TA instrument Co. and by a successive self-nucleation/annealing (SSA) measurement method.

Particularly, in the first cycle, the temperature was elevated to 150° C., kept for 1 minute, and reduced to −100° C. In the second cycle, the temperature was elevated to 120° C., kept for 30 minutes, and reduced to −100° C. In the third cycle, the temperature was elevated to 110° C., kept for 30 minutes, and reduced to −100° C. As described above, a process of elevating the temperature and decreasing to −100° C. by an interval of 10° C. was repeated to −60° C. so as to crystallize in each temperature section.

In the last cycle, the temperature was elevated to 150° C., and heat capacity was measured.

The temperature-heat capacity curve thus obtained was integrated by each section, and the heat capacity of each section with respect to total heat capacity was fractionated. Here, the temperature at which 50% of the total is melted is defined as T(50), 90% of the total is melted is defined as T(90), and 95% of the total is melted is defined as T(95).

FIG. 3 shows an SSA graph of the polymer of Example 1, and FIG. 4 shows an SSA graph of the polymer of Comparative Example 1.

FIG. 5 shows a fractionated graph of the SSA results of the polymer of Example 1, and FIG. 6 shows a fractionated graph of the SSA results of the polymer of Comparative Example 1.

6) Hardness (Shore A)

Hardness was measured according to the standard of ASTM D2240 using GC610 STAND for durometer of TECLOCK Co. and a shore durometer Type A of Mitutoyo Co.

7) Tensile Strength and Tearing Strength of Polymer

The olefin-based copolymers of Example 1 and Comparative Examples 1 to 3 were extruded to manufacture pallet shapes, and tensile strength and tearing strength when broken were measured according to ASTM D638 (50 mm/min).

TABLE 2 DSC SSA Density MI Mw Tm T(90) − T(95) − (g/mL) (g/10 min) (g/mol) MWD (° C.) T(50) T(90) T(95) T(50) T(90) Example 1 0.862 1.20 106,000 2.01 32.1 16.0 51.1 67.6 35.1 16.5 Example 2 0.866 4.39 69,070 2.07 33.0 19.8 57.4 83.8 37.6 26.4 Example 3 0.872 1.22 99,068 2.05 45.9 31.1 61.9 73.0 30.8 11.1 Example 4 0.866 3.30 70,000 2.11 37.8 22.9 54.6 64.9 31.7 10.3 Example 5 0.865 5.10 75,388 2.09 37.2 23.1 54.1 65.3 31.0 11.2 Comparative 0.861 1.32 105,000 1.98 39.7 20.1 48.4 54.6 28.3 6.2 Example 1 Comparative 0.861 1.12 102,000 2.11 28.6 14.7 46.0 54.9 31.3 8.9 Example 2 Comparative 0.862 1.20 91,419 2.18 28.5 15.7 46.6 55.3 30.9 8.7 Example 3 Comparative 0.862 1.23 100,423 2.185 29.9 15.0 47.8 54.2 32.8 6.4 Example 4 Comparative 0.869 1.20 92,000 2.04 49.3 32.3 57.1 64.4 24.8 7.3 Example 5 Comparative 0.865 3.40 71,000 2.04 43.8 21.5 54.2 57.8 32.7 3.6 Example 6 Comparative 0.868 5.10 76,735 2.14 44.2 23.2 54.6 61.9 31.4 7.3 Example 7

TABLE 3 DSC SSA Density MI Tm T(90) − T(95) − Tensile Tearing Hardness (g/mL) (g/10 min) (° C.) T(50) T(90) strength strength (Shore A) Example 1 0.862 1.20 32.1 35.1 16.5 2.2 29.5 55.0 Comparative 0.861 1.32 39.7 28.3 6.2 2.1 25.6 56.7 Example 1 Comparative 0.861 1.12 28.6 31.3 8.9 1.6 22.4 52.9 Example 2 Comparative 0.862 1.20 28.5 30.9 8.7 1.3 16.7 51.6 Example 3

When comparing Example 1 and Comparative Example 1 having the equivalent degrees of density and MI, FIG. 1 and FIG. 2 measured by DSC showed analogical tendency and similar graph types, and no significant difference was confirmed. However, in FIG. 3 and FIG. 4 measured by SSA, it could be confirmed that there was a significant difference in a high temperature region of 75° C. or more. Particularly, Example 1 showed peaks at 75° C. or more, but the Comparative Example did not show. Comparative Example 2 and Comparative Example 3 showed peaks in the corresponding region, but the sizes were small when compared with the Example. Tt could be found that due to the difference of melting in the high temperature region, Examples 1 to 5 satisfied T(90)−T(50)≤50, also satisfied T(95)−T(90)≥10, and had wide values in T(95)−T(90) when compared with Comparative Examples 1 to 7.

Through Table 3, the mechanical strength of Example 1 and Comparative Examples 1, 2, and 3, having equivalent degrees of density and MI may be compared. It could be found that Example 1 introduced a polymer melted at a high temperature and showed increased mechanical rigidity, and thus, attained increased tensile strength and tearing strength when compared with Comparative Examples 1 to 3.

Examples 1 to 5 correspond to polymers obtained by polymerizing an olefin-based monomer by injecting a hydrogen gas and introducing a highly crystalline region. Accordingly, T(90)−T(50)≤50 is satisfied, T(95)−T(90)≥10 is also satisfied, and high mechanical rigidity is shown. It could be confirmed that the satisfaction or not of T(90)−T(50)≤50 and T(95)−T(90)≥10 and the mechanical rigidity could be changed according to the injection or not of the hydrogen gas and the injection amount thereof during polymerization, through comparing with Comparative Example 2 and Comparative Example 4.

In addition, if the olefin-based polymer of the present invention is included in a polypropylene-based composite, a polypropylene-based composite showing markedly improved impact strength properties together with excellent mechanical strength may be provided. Hereinafter, experiments on applying the olefin-based polymer of the present invention in a polypropylene-based composite are shown.

Composite Preparation Example 1: Preparation of Polypropylene-Based Composite

To 20 parts by weight of the olefin copolymer prepared in Example 1, 60 parts by weight of highly crystalline impact copolymer polypropylene (CB5230, Korea Petrochemical Industrial Co. Ltd.) having a melt index (230° C., 2.16 kg) of 30 g/10 min, and 20 parts by weight of talc (KCNAP-400™, Coats Co.) (average particle diameter (D₅₀)=11.0 μm) were added, and then, 0.1 parts by weight of AO1010 (Ciba Specialty Chemicals) as an antioxidant, 0.1 parts by weight of tris(2,4-di-tert-butylphenyl)phosphite (A0168), and 0.3 parts by weight of calcium stearate (Ca-St) were added. Then, the resultant mixture was melted and mulled using a twin screw extruder to prepare a polypropylene-based composite compound in a pellet shape. In this case, the twin screw extruder has a diameter of 25 (and a ratio of length to diameter of 40, and conditions were set to a barrel temperature of 200° C. to 230° C., a screw rotation velocity of 250 rpm, and an extrusion rate of 25 kr/hr.

Composite Preparation Examples 2 to 5: Preparation of Polypropylene-Based Composites

Polypropylene-based composites were prepared by the same method as in Example 1 except for using the olefin copolymers shown in Table 4 below instead of the olefin copolymer prepared in Example 1. In this case, the type of polypropylene, and the ratio of olefin copolymer and polypropylene were changed in Example 5. In Table 4 below, polypropylene represented by CB5290 is highly crystalline impact copolymer polypropylene (CB5290, Korea Petrochemical Industrial Co. Ltd.) having a melt index (230° C., 2.16 kg) of 90 g/10 min.

Composite Comparative Preparation Examples 1 to 7: Preparation of Polypropylene-Based Composites

Polypropylene-based composites were prepared by the same method as in Example 1 except for using the olefin copolymers shown in Table 4 below instead of the olefin copolymer prepared in Preparation Example 1. In this case, the type of polypropylene, and the ratio of olefin copolymer and polypropylene were changed in Comparative Example 7.

In Table 4 below, polypropylene represented by CB5290 is highly crystalline impact copolymer polypropylene (CB5290, Korea Petrochemical Industrial Co. Ltd.) having a melt index (230° C., 2.16 kg) of 90 g/10 min.

TABLE 4 Compounding ratio Olefin-based Olefin-based polymer PP Talc polymer polypropylene (wt %) (wt %) (wt %) Composite Preparation Example 1 CB5230 20 60 20 Example 1 Composite Preparation Example 3 CB5230 20 60 20 Example 2 Composite Preparation Example 4 CB5230 20 60 20 Example 3 Composite Preparation Example 5 CB5230 20 60 20 Example 4 Composite Preparation Example 3 CB5290 30 50 20 Example 5 Composite Comparative Comparative CB5230 20 60 20 Preparation Example 1 Example 1 Composite Comparative Comparative CB5230 20 60 20 Preparation Example 2 Example 2 Composite Comparative Comparative CB5230 20 60 20 Preparation Example 3 Example 3 Composite Comparative Comparative CB5230 20 60 20 Preparation Example 4 Example 5 Composite Comparative Comparative CB5230 20 60 20 Preparation Example 5 Example 6 Composite Comparative Comparative CB5230 20 60 20 Preparation Example 6 Example 7 Composite Comparative Comparative CB5290 30 50 20 Preparation Example 7 Example 5

Experimental Example 2: Evaluation of Physical Properties of Polypropylene-Based Composite

In order to confirm the physical properties of the polypropylene-based composites prepared in Composite Preparation Examples 1 to 5, and Composite Comparative Preparation Examples 1 to 7, specimens were manufactured by injection molding the polypropylene-based composites using an injection machine at a temperature of 230° C., and the specimens were stood in a constant temperature and humidity room for 1 day, and then, the specific gravity of polymers, the melt index of polymers, tensile strength, flexural strength and flexural modulus, impact strength at low temperature and room temperature, and contraction ratio were measured. The physical properties of the specimens thus manufactures are shown in Table 5 below.

1) Specific Gravity

Measurement was conducted according to ASTM D792.

2) Melt Index (MI) of Polymer

The melt index (MI) of a polymer was measured according to ASTM D-1238 (condition E, 230° C., 2.16 kg load).

3) Tensile Strength and Flexural Strength

Measurement was conducted using INSTRON 3365 apparatus according to ASTM D790.

4) Impact Strength at Low Temperature and at Room Temperature

Measurement was conducted according to ASTM D256, impact strength at room temperature was measured under room temperature (23° C.) conditions, and impact strength at low temperature was measured in a low-temperature chamber (−30° C.) after standing for 12 hours or more.

TABLE 5 Impact strength Impact strength Specific MI Tensile Flexural at low at room gravity (g/10 min) strength strength temperature temperature Composite 1.033 14.3 211 341 4.7 42.1 Preparation Example 1 Composite 1.041 14.6 211 336 4.7 43.9 Preparation Example 2 Composite 1.030 13.9 206 334 4.8 42.5 Preparation Example 3 Composite 1.038 13.9 205 327 4.7 40.9 Preparation Example 4 Composite 1.037 14.6 219 344 3.6 34.5 Preparation Example 5 Composite 1.03 15.0 216 340 3.8 37.3 Comparative Preparation Example 1 Composite 1.032 17.0 239 336 3.8 34.8 Comparative Preparation Example 2 Composite 1.032 17.4 238 334 3.8 34.5 Comparative Preparation Example 3 Composite 1.036 17.7 217 336 4.3 32.9 Comparative Preparation Example 4 Composite 1.031 17.8 217 333 4.4 33.1 Comparative Preparation Example 5 Composite 1.031 16.2 171 246 8.4 53.7 Comparative Preparation Example 6 Composite 1.033 16.7 168 241 9.0 52.8 Comparative Preparation Example 7

Referring to Table 5, when Comparing the polypropylene-based composites including olefin-based copolymers having equivalent degrees of density and MT values, it could be confirmed that the polypropylene-based composites prepared by using the olefin-based polymers of the Examples maintained similar degrees of impact strength at low temperature and impact strength at room temperature, and improved mechanical strength such as tensile strength and flexural strength when compared with the polypropylene-based composites prepared by using the olefin-based polymers of the Comparative Examples. Through this, it could be confirmed that the mechanical rigidity of a polypropylene-based composite may be improved by including an olefin-based copolymer introducing a highly crystalline region and showing high mechanical rigidity of the Example in a polypropylene-based composite. 

1. An olefin-based polymer satisfying the following conditions (1) to (3): (1) a melt index (MI, 190° C., 2.16 kg load conditions) is from 0.1 g/10 min to 10.0 g/10 min, (2) a density (d) is from 0.860 g/cc to 0.880 g/cc, and (3) T(90)−T(50)≤50 and T(95)−T(90)≥10, wherein T(50), T(90) and T(95) are temperatures at which 50%, 90%, and 95% of the olefin-based polymer are melted, respectively, when fractionating a temperature-heat capacity curve from measurement results by a differential scanning calorimetry precise measurement method (SSA).
 2. The olefin-based polymer according to claim 1, wherein the olefin-based polymer additionally satisfies the following conditions: (4) a weight average molecular weight (Mw) is from 10,000 g/mol to 500,000 g/mol.
 3. The olefin-based polymer according to claim 1, wherein the olefin-based polymer additionally satisfies the following conditions: (5) a molecular weight distribution (MWD) is from 0.1 to 6.0.
 4. The olefin-based polymer according to claim 1, wherein the olefin-based polymer additionally satisfies the following conditions: (6) a melting temperature is from 20° C. to 70° C. when measuring differential scanning calorimetry (DSC).
 5. The olefin-based polymer according to claim 1, wherein the melt index (MI) of the olefin-based polymer is 0.3 g/10 min to 5.5 g/10 min.
 6. The olefin-based polymer according to claim 1, wherein the olefin-based polymer satisfies 30≤T(90)−T(50)≤40 and 10≤T(95)−T(90)≤20 when measured by a differential scanning calorimetry precise measurement method (SSA).
 7. The olefin-based polymer according to claim 1, wherein the olefin-based polymer is a copolymer of ethylene and an alpha-olefin comonomer of 3 to 12 carbon atoms.
 8. The olefin-based polymer according to claim 7, wherein the alpha-olefin comonomer comprises any one selected from the group consisting of propylene, 1-butene, 1-pentene, 4-methyl-1-pentene, 1-hexene, 1-heptene, 1-octene, 1-decene, 1-undecene, 1-dodecene, 1-tetradecene, 1-hexadecene, 1-eicosene, norbornene, norbonadiene, ethylidene norbornene, phenyl norbornene, vinyl norbornene, dicyclopentadiene, 1,4-butadiene, 1,5-pentadiene, 1,6-hexadiene, styrene, alpha-methylstyrene, divinylbenzene and 3-chloromethylstyrene, or mixtures of two or more thereof.
 9. The olefin-based polymer according to claim 1, wherein the olefin-based polymer is a copolymer of ethylene and 1-butene.
 10. An olefin-based polymer satisfying the following: a melt index (MI) is from 0.4 g/10 min to 7.0 g/10 min; a density (d) is from 0.860 g/cc to 0.880 g/cc; 20≤T(90)−T(50)≤45 and 10≤T(95)−T(90)≤30 wherein T(50), T(90) and T(95) are temperatures at which 50%, 90%, and 95% of the olefin-based polymer are melted, respectively, when fractionating a temperature-heat capacity curve from measurement results by a differential scanning calorimetry precise measurement method (SSA); a weight average molecular weight (Mw) is from 10,000 to 500,000 g/mol; a molecular weight distribution (MWD) is from 0.1 to 6.0; and a melting temperature when measuring differential scanning calorimetry (DSC) is from 20° C. to 60° C.
 11. The olefin-based polymer according to claim 1, wherein the olefin-based polymer is an olefin-based polymer obtained by a preparation method comprising: polymerizing an olefin-based monomer by injecting a hydrogen gas in the presence of a catalyst composition for polymerizing olefin, the catalyst composition comprising a transition metal compound of the following Formula 1:

in Formula 1, R₁ groups are the same or different and each independently hydrogen, alkyl of 1 to 20 carbon atoms, alkenyl of 2 to 20 carbon atoms, aryl, silyl, alkylaryl, arylalkyl, or metalloid radical of a metal in group 4, which is substituted with hydrocarbyl, and two R₁ groups are optionally connected with each other by alkylidene radical containing alkyl of 1 to 20 carbon atoms or aryl radical of 6 to 20 carbon atoms to form a ring; R₂ groups are the same or different and each independently hydrogen; halogen; alkyl of 1 to 20 carbon atoms; aryl; alkoxy; aryl oxy; or amido radical, and two R₂ groups are optionally connected with each other to form an aliphatic ring or an aromatic ring; R₃ groups are the same or different and each independently hydrogen; halogen; alkyl of 1 to 20 carbon atoms; or a nitrogen-containing aliphatic or aromatic ring, which is unsubstituted or substituted with aryl radical, two or more R₃ groups are optionally connected with each other to form an aliphatic or aromatic ring; M is a transition metal in group 4; and Q₁ and Q₂ are each independently halogen; alkyl of 1 to 20 carbon atoms; alkenyl; aryl; alkylaryl; arylalkyl; alkyl amido of 1 to 20 carbon atoms; aryl amido; or alkylidene radical of 1 to 20 carbon atoms.
 12. The olefin-based polymer according to claim 11, wherein the olefin-based polymer is prepared by continuous solution polymerization reaction using a continuous stirred tank reactor by injecting hydrogen in the presence of the catalyst composition for polymerizing olefin.
 13. An olefin-based polymer satisfying the following: a melt index (MI) is from 0.4 g/10 min to 7.0 g/10 min; a density (d) is from 0.860 g/cc to 0.880 g/cc; and 30≤T(90)−T(50)≤40 and 10≤T(95)−T(90)≤20 wherein T(50), T(90) and T(95) are temperatures at which 50%, 90%, and 95% of the olefin-based polymer are melted, respectively, when fractionating a temperature-heat capacity curve from measurement results by a differential scanning calorimetry precise measurement method (SSA), wherein the olefin-based polymer is an olefin-based polymer obtained by a preparation method comprising: polymerizing an olefin-based monomer by injecting a hydrogen gas in the presence of a catalyst composition for polymerizing olefin, the catalyst composition comprising a transition metal compound of the following Formula 1:

in Formula 1, R₁ groups are the same or different and each independently hydrogen, alkyl of 1 to 20 carbon atoms, alkenyl of 2 to 20 carbon atoms, aryl, silyl, alkylaryl, arylalkyl, or metalloid radical of a metal in group 4, which is substituted with hydrocarbyl, and two R₁ groups are optionally connected with each other by alkylidene radical containing alkyl of 1 to 20 carbon atoms or aryl radical of 6 to 20 carbon atoms to form a ring; R₂ groups are the same or different and each independently hydrogen; halogen; alkyl of 1 to 20 carbon atoms; aryl; alkoxy; aryl oxy; or amido radical, and two among R₂ groups are optionally connected with each other to form an aliphatic ring or an aromatic ring; R₃ groups are the same or different and each independently hydrogen; halogen; alkyl of 1 to 20 carbon atoms; or a nitrogen-containing aliphatic or aromatic ring, which is unsubstituted or substituted with aryl radical, two or more R₃ groups are optionally connected with each other to form an aliphatic or aromatic ring; M is a transition metal in group 4; and Q₁ and Q₂ are each independently halogen; alkyl of 1 to 20 carbon atoms; alkenyl; aryl; alkylaryl; arylalkyl; alkyl amido of 1 to 20 carbon atoms; aryl amido; or alkylidene radical of 1 to 20 carbon atoms.
 14. The olefin-based polymer according to claim 13, wherein the olefin-based polymer is obtained by a preparation method in which an injection amount of the hydrogen gas is 0.35 to 3 parts by weight based on 1 part by weight of the olefin-based monomer.
 15. The olefin-based polymer according to claim 7, wherein the alpha-olefin is included in an amount of 90 wt % or less, based on the total weight of the copolymer.
 16. The olefin-based polymer according to claim 11, wherein the transition metal compound of Formula 1 is Formula 1-1 below: 